Polyphenylene Oxide PPO Resin / PPO Granules manufacturer factory price
OverviewQuick DetailsPlace of Origin:China (Mainland)PackagingDeliveryPackaging Details25kg/bag or as customer's requestDelivery Timewit
$720 /MetricTon
Product Details
Transaction Comments
Polyphenylene Oxide PPO Resin / PPO Granules
1. Specification:
ITEM | TEST CONDITION | TEST METHOD | DATA | UNIT | ||
Physical properties | Proportion |
| ASTM D792 | 1.09 |
| |
Water absorption | 24hrs | ASTM D570 | 0.06 | % | ||
Mold Shrinkage | 3.2mm | ASTM D955 | 5-7 | E-3 | ||
Mechanical properties | Tensile strength | 3.2mm | ASTM D638 | 75 | MPa | |
Elongation | 3.2mm | ASTM D638 | 18 | % | ||
Bending Strength | 6.4mm | ASTM D790 | 112 | MPa | ||
Flexural modulus | 6.4mm | ASTM D790 | 2646 | MPa | ||
Notched impact strength | 23°C | ASTM D256 | 160 | J/M | ||
Electrical properties | Loss Factor | 60Hz | ASTM D150 | - | - | |
Permittivity | 1MHz | ASTM D150 | 2.49 |
| ||
Volume resistivity |
| ASTM D257 | 2.0E+16 | ohm·cm | ||
Surface resistance |
| D257 | 1.0E+16 | ohm·cm | ||
Thermal properties | Heat distortion temperature | 0.45MPa | ASTM D648 | 133 | °C | |
Heat distortion temperature | 1.80MPa | ASTM D648 | 125 | °C | ||
Vicat Softening Point |
| ASTM D1525 | 150 | °C | ||
UL Long-term use temperature | Electric |
| UL746B | 105 | °C | |
Including the impact |
| UL746B | 100 | °C | ||
No impact |
| UL746B | 105 | °C | ||
Flammability |
| UL94 | V-0 |
| ||
2. Materials properties:
1.Good overall performance, can be used in 120-degree steam, electrical insulation, water is small, but there is a tendency to stress cracking. Noryl eliminate stress cracking.
2, there are outstanding electrical insulation and water resistance, good dimensional stability. The dielectric properties of plastics in the first place.
3. Have a higher heat resistance, glass transition temperature of 211 degrees, melting point of 268 degrees, heated to 330 degrees decomposition tendency to higher levels PPO its better heat resistance, heat distortion temperature up to 190 degrees.
4, good flame retardant, self-extinguishing, with HIPS mixed with moderate flammability. Lightweight, non-toxic and can be used in the food and drug industries. Poor resistance to rotation, for a long time in the sun will change.
5, the modification can be blended with ABS, HDPE, PPS, PA, HIPS, glass fibers etc.