HIPS granules
Origin Thailand
High Impact Polystyrene
Melt Flow Index (5 kg/200 deg.C):3.0 g/10min.
Izod Notched Impact (1/4", 23 deg.C) :12Kg-cm/cm
Tensile Strength at Yield (23C): 218 kg/cm2
Flexural Strength at Yield (23 deg.C): 422kg/cm2
Flexural Modulus (23 deg.C) :2.18 ×104kg/cm2
Rockwell Hardness (1/4", 23 deg.C):82 L-Scale
Heat Distortion Temperature (1/4", 18.6 kg/cm2) 90 deg.C
Vicat Softening Temperature (1/8", kg):96 deg.C