Grade

C

Mn

P

S

Si

Cr

Ni

Cu

100Cr6

0.93-1.05

0.25-0.45

0.025 max

0.015 max

0.15-0.35

1.35-1.60

0.30 max

0.30 max

Packing details

In seaworthy packing, as your requirement.

Delivery details

within 10-50 days

>>>Heat Treatment:

Forging: 100Cr6 bearing steel is forged at 1950 – 2100ºF (1065 – 1150ºC), and should not be forged below 1700ºF (925ºC.) A post-forge equalization treatment is recommended at 1375ºF (745ºC) for 4-6 hours followed by air cooling.

Annealing: 100Cr6 bearing steel is annealed at 872°C (1600°F) followed by slowly cooling to reduce cold working or machining stress.

Hardening: 100Cr6 bearing steel is hardened by cold working, or heating and quenching. It can be carburized at 913°C (1675°F) followed by quenching. It is again heated at 788°C (1450°F) followed by quenching for the second time.

>>>Steel Grades

52100 

DIN1.3505

100Cr6

 AISI L3

Mill′s test certificate:

EN 10204/3.1 with all relevant data reg. chem. composition, mech. properties and results of testing.

Application:

Bearing steel is primarily used for the manufacture of aircraft bearings and other highly stressed parts. It has the good rolling fatigue strength required at operating temperatures less than 400ºF (200ºC). The grade is preferably vacuum arc re-melted to give optimum performance.